T/CPF 0096-2025 包装用单一材质单向拉伸聚乙烯复合膜、袋

　　T/CPF 0096—2025　　包装用单一材质单向拉伸聚乙烯复合膜、袋

　　Mono material machine direction oriented polyethylene laminated film

　　and pouch for packaging

　　2025-02-17 发布2025-02-17 实施

　　中国包装联合会 发 布

　　目 次

　　前言 ····························································································································· II

　　1 范围 ·························································································································· 1

　　2 规范性引用文件 ·········································································································· 1

　　3 术语和定义 ················································································································· 2

　　4 缩略语与符号·············································································································· 2

　　5 分类 ·························································································································· 2

　　6 技术要求 ···················································································································· 3

　　7 试验方法 ···················································································································· 5

　　8 检验规则 ···················································································································· 8

　　9 标志、包装、运输和贮存 ······························································································ 9

　　参考文献 ······················································································································ 10

　　T/CPF 0096—2025

　　II

　　前 言

　　本文件按照GB/T 1.1—2020《标准化工作导则 第1 部分：标准化文件的结构和起草规则》的

　　规定起草。

　　请注意本文件的某些内容可能涉及专利。本文件的发布机构不承担识别专利的责任。

　　本文件由中国包装联合会提出并归口。

　　本文件起草单位：诚德科技股份有限公司、嘉兴星越包装材料有限公司、中国出口商品包装研

　　究所、湖南省长城铭泰新材料科技有限公司、上海乐朗检测技术有限公司、阿美特克商贸(上海)

　　有限公司、河南耐可达彩色印刷有限公司、安姆科科技研发有限公司、广州通泽机械有限公司、浙

　　江翔鹏新材料有限公司、纳爱斯集团有限公司、广东道科新材料科技有限公司、中包包装行业生产

　　力促进中心有限公司、埃克森美孚化工商务(上海)有限公司、上海紫江彩印包装有限公司、河北

　　北人新材科技股份有限公司、济南浩科仪器有限公司、四川美丰化工股份有限公司、南京沪江复合

　　材料股份有限公司、浙江海顺新材料有限公司、莱芬豪舍塑料机械(苏州)有限公司、广东仕诚塑

　　料机械有限公司、东昌工业(临海)有限公司、永新股份(黄山)包装有限公司、中国包装联合会

　　塑料包装专业委员会、济南思克测试技术有限公司、华煊标准技术服务(苏州)有限公司。

　　本文件主要起草人：王道德、冯志伟、冯清正、刘天航、毛兵、武晓庆、姚船、姜鹤、何志勇、

　　王忠林、葛世安、林桃根、陈漫里、杨浩文、刘策、王陈庚、杨涛、郑定杰、仇凯、王慢慢、陈华、

　　吕晨阳、胡正阳、迟少龙、胡勇、杨金龙、陈付兵、周云帆、张春华、李岳、曹斐、张目清、王晓梅、

　　蒋娜、孟李军。

　　T/CPF 0096—2025

　　1

　　包装用单一材质单向拉伸聚乙烯复合膜、袋

　　1 范围

　　本文件界定了包装用单一材质单向拉伸聚乙烯复合膜、袋(以下简称“复合膜、袋”)的术语

　　和定义，给出了缩略语和分类，描述了试验方法，规定了技术要求及检验规则、标志、包装、运输

　　和贮存的要求。

　　本文件适用于包装用单一材质单向拉伸聚乙烯复合膜、袋的设计、生产和检验。

　　2 规范性引用文件

　　下列文件中的内容通过文中的规范性引用而构成本文件必不可少的条款。其中，注日期的引用

　　文件，仅该日期对应的版本适用于本文件;不注日期的引用文件，其最新版本(包括所有的修改单)

　　适用于本文件。

　　GB/T 191 包装储运图示标志

　　GB/T 1037 塑料薄膜与薄片水蒸气透过性能测定 杯式增重与减重法

　　GB/T 1038.1 塑料制品 薄膜和薄片 气体透过性试验方法 第1 部分：差压法

　　GB/T 1040.3 塑料拉伸性能的测定 第3 部分：薄膜和薄片的试验条件

　　GB/T 2828.1—2012 计数抽样检验程序 第1 部分：按接收质量限(AQL)检索的逐批检验抽

　　样计划

　　GB/T 2918—2018 塑料 试样状态调节和试验的标准环境

　　GB/T 6672 塑料薄膜和薄片 厚度测定 机械测量法

　　GB/T 6673 塑料薄膜和薄片长度和宽度的测定

　　GB/T 7707 凹版装潢印刷品

　　GB 8808—1988 软质复合塑料材料剥离试验方法

　　GB/T 8809 塑料薄膜抗摆锤冲击试验方法

　　GB/T 10004 包装用塑料复合膜、袋 干法复合、挤出复合

　　GB/T 10006 塑料 薄膜和薄片 摩擦系数的测定

　　GB 12904 商品条码 零售商品编码与条码表示

　　GB/T 15171 软包装件密封性能试验方法

　　GB/T 17497.2 柔性版装潢印刷品 第2 部分：塑料与金属箔类

　　GB/T 18348 商品条码 条码符号印制质量的检验

　　GB/T 19789 包装材料 塑料薄膜和薄片氧气透过性试验 库仑计检测法

　　GB/T 26253 塑料薄膜和薄片水蒸气透过率的测定 红外检测器法

　　QB/T 1130 塑料直角撕裂性能试验方法

　　QB/T 2358 塑料薄膜包装袋热合强度试验方法

　　T/CPF 0096—2025

　　2

　　3 术语和定义

　　下列术语和定义适用于本文件。

　　3.1

　　单一材质 mono material

　　单一类型聚合物占总材料质量大于90%的塑料材料，其他材料占总材料质量小于10%，且任意

　　一种其他材料占总材料质量不超过5%。

　　注：其他材料为不含有PVC、PET、PVDC、PA 等的材料。

　　4 缩略语与符号

　　下列缩略语适用于本文件。

　　PE——聚乙烯;

　　PVC——聚氯乙烯;

　　PET——聚对苯二甲酸乙二醇酯;

　　PVDC——聚偏二氯乙烯;

　　EVOH——乙烯-乙烯醇共聚物;

　　MDO——单向(纵向)拉伸;

　　MDOPE——单向(纵向)拉伸聚乙烯共挤薄膜;

　　PE/EVOH——聚乙烯/乙烯-乙烯醇共聚物共挤薄膜;

　　MDO(PE/EVOH)——单向(纵向)拉伸聚乙烯/乙烯-乙烯醇共聚物共挤薄膜。

　　下列符号适用于本文件。

　　“+”——在基材膜上进行二次加工涂布或者蒸镀工艺;

　　“/”——表示共挤;

　　“//”——表示复合。

　　5 分类

　　5.1 按形状分类

　　产品按形状分类可分为膜和袋，膜分为卷膜和片膜。

　　5.2 按层数分类

　　产品按复合层数分为双层和多层两大类，其中双层分为A1～A5 五种，多层分为B1～B6 六种，

　　结构类别见表1。

　　表1 结构类别

　　层数 代号 结构

　　双层

　　A1 MDOPE//PE

　　A2 MDOPE//PE/EVOH

　　A3 MDOPE+EVOH//PE

　　A4 MDOPE+阻隔层(涂布)//PE

　　A5 MDOPE+阻隔层(蒸镀)//PE

　　T/CPF 0096—2025

　　3

　　表1 结构类别(续)

　　层数 代号 结构

　　多层

　　B1 MDOPE//MDOPE//PE

　　B2 MDOPE+涂层//MDOPE//PE

　　B3 MDOPE+镀层//MDOPE//PE

　　B4 MDOPE//MDOPE+涂层//PE

　　B5 MDOPE//MDOPE+镀层//PE

　　B6 MDOPE//MDOPE//PE+EVOH

　　6 技术要求

　　6.1 外观

　　产品外观应符合表2 的要求。

　　表2 外观要求

　　项目

　　要求

　　膜 袋

　　划伤、烫伤、桔皮、孔洞、僵块、分层、裂纹、

　　粘连或缺损 不应有

　　尘埃、杂质、异物、油渍或不洁物等污染 不应有

　　折皱 允许有轻微的间断折皱，但不多于产品面积的5%

　　热封部位 — 平整、无虚封、无明显气泡

　　膜卷松紧 搬动时不出现膜间滑动 —

　　膜卷暴筋 允许有不影响使用的轻微暴筋—

　　膜卷端面不平整度 ≤2 mm —

　　膜卷每卷接头数/个

　　复合膜长小于500 m 时不多于1

　　个，不小于500 m 时不多于2 个。

　　接头处应牢固并有明显标记

　　—

　　注：“—”为不适用。

　　6.2 印刷质量

　　6.2.1 凹版印刷

　　凹版装潢印刷质量应符合GB/T 7707 的规定。

　　6.2.2 柔性版印刷

　　柔性版装潢印刷质量应符合GB/T 17497.2 的规定。

　　6.2.3 条码印刷

　　条码印刷质量应符合GB 12904 的规定。

　　6.3 尺寸及偏差

　　复合膜、袋尺寸及偏差应符合表3 的要求。

　　T/CPF 0096—2025

　　4

　　表3 尺寸及偏差

　　项目 卷膜 片膜

　　袋的长度/mm

　　<100 100～400 401～600 >600

　　厚度平均偏差/% ±10 ±10 ±10 ±10 ±10 ±10

　　宽度偏差/mm ±2.0 ±1.0 ±2.0 ±4.0 ±5.0 ±6.0

　　长度偏差/mm 无负偏差 ±2.0 ±2.0 ±4.0 ±5.0 ±6.0

　　印刷图案间距偏差/% ±5.0 — — — — —

　　封边宽度偏差/% — — ±20 ±20 ±20 ±20

　　封口与袋边距离/mm — — ≤3 ≤4 ≤5 ≤6

　　注：“—”为不适用。

　　6.4 物理机械性能

　　6.4.1 剥离强度、热合强度、拉断力、断裂标称应变、直角撕裂力、抗摆锤冲击能指标应符合表4 的

　　要求。水蒸气透过量、氧气透过率指标应符合表5 的要求。表1 规定结构之外的由供需双方协商确定。

　　表4 剥离强度、热合强度、拉断力、断裂标称应变、直角撕裂力、抗摆锤冲击能和摩擦系数

　　结构类型 剥离强度

　　N/15 mm

　　热合强度

　　N/15 mm

　　拉断力/N 断裂标称应变/% 直角撕裂力/N 抗摆锤冲

　　纵向 横向 纵向 横向 纵向 横向 击能/J

　　双层 ≥1.0 ≥10.0 ≥30 ≥20 ≥35 ≥5 ≥1.5 ≥0.6

　　多层 ≥1.0 ≥10.0 ≥30 ≥20 ≥35 ≥10 ≥3.0 ≥0.6

　　摩擦系数 摩擦系数(内面/钢板 静/动)应≤0.40，特殊需求可由供需双方协商确定

　　气密性 无渗漏

　　注1：无法剥离视为合格。

　　注2：对气密性有要求的产品应做气密性测试。

　　表5 水蒸气透过量、氧气透过率

　　结构类型 水蒸气透过量

　　[g/(m2·24 h)]≤

　　氧气透过率

　　[cm3/(m2·24 h·0.1 mPa)]≤

　　A1 10.0 1 000

　　A2 4.0 3.0

　　A3 4.0 3.0

　　A4 3.0 1.0

　　A5 3.0 10.0

　　B1 10.0 1 000

　　B2 3.0 1.0

　　B3 3.0 10.0

　　B4 3.0 1.0

　　B5 3.0 10.0

　　B6 4.0 3.0

　　T/CPF 0096—2025

　　5

　　6.4.2 耐压性能

　　袋的内容物为粉体、液体或需要做充气、抽真空包装时，耐压性能指标应符合表6 的要求。

　　表6 袋的耐压性能

　　袋与内装物总质量/g

　　负荷/N

　　要求

　　三边封袋 其他袋

　　<30 100 80

　　无渗漏、不破裂

　　30～100 200 120

　　101～400 400 200

　　>400 600 300

　　6.4.3 跌落性能

　　袋的内容物为粉体、液体或需要做充气、抽真空包装时，跌落性能指标应符合表7 的要求。

　　表7 袋的跌落性能

　　袋与内装物总质量/g 跌落高度/mm 要求

　　<100 800

　　101～400 500 不破裂

　　>400 300

　　6.4.4 摩擦系数

　　摩擦系数(内面/钢板 静/动)应≤0.40，特殊需求可由供需双方协商确定。

　　6.4.5 耐热性能

　　对于有耐热要求且使用温度为80 ℃以上的产品经耐热试验后，应无明显变形、层间剥离、热

　　封部位剥离现象。

　　6.4.6 耐高温介质

　　使用温度为80 ℃以上、90 ℃以下的产品经耐高温介质试验后，应无分层、破损、袋内外无明

　　显变形。剥离强度、拉断力、断裂标称应变和热合强度下降率应不大于30%。

　　7 试验方法

　　7.1 样品准备

　　取样数量须足够完成试验的项目。卷膜取样时去掉表面三层，再沿膜卷的宽度方向切割取样。

　　用纸芯卷好，必要时标记处理面。

　　样品的状态调节按GB/T 2918—2018 的规定进行。温度在18 ℃～28 ℃的室温条件下，状态调

　　节时间不小于16 h，并在此条件下进行试验。

　　7.2 外观

　　在自然光线下目测，并用精度不低于0.5 mm 的量具测量。

　　7.3 印刷

　　7.3.1 凹版印刷

　　按GB/T 7707 的规定进行。

　　T/CPF 0096—2025

　　6

　　7.3.2 柔性版印刷

　　按GB/T 17497.2 的规定进行。

　　7.3.3 条码印刷

　　商品条码按GB/T 18348 的规定进行检验。

　　7.4 尺寸及偏差

　　7.4.1 长度、宽度及印刷图案间距偏差按GB/T 6673 的规定进行。钢直尺上的零标记对准材料左

　　纵向边，检查其完全调准，移动到材料右边，检查材料对边的位置，以校正其在平面基准刻度上

　　的位置，读取与材料右边相距最近的最后一个毫米数值，钢直尺的零刻度与基准刻度上所读取的

　　最后一个毫米数值重合，用钢直尺测出重合点与材料右边缘之间的宽度，刻度为0.1 mm。

　　7.4.2 厚度偏差按GB/T 6672 的规定进行。按等分试样长度的方法以确定测量厚度的位置点，方

　　法如下：

　　a)试样长度<300 mm，测10 点;

　　b)试样长度在300 mm～1 500 mm 之间，测20 点;

　　c)试样长度>1 500 mm，至少测30 点。

　　对未裁边的样品，应在距边50 mm 开始测量。

　　7.4.3 袋的封边宽度偏差使用精度不低于0.5 mm 的量具测量。

　　7.4.4 袋的封口与袋边的距离用精度不低于0.5 mm 的量具测量。

　　7.5 物理力学性能

　　7.5.1 剥离力

　　按GB/T 8808—1998 中A 法的规定进行。试样宽度为15.0 mm±0.1 mm，长度为200 mm，试验

　　速度为300 mm/min±50 mm/min。

　　7.5.2 热合强度

　　按QB/T 2358 的规定进行。复合膜的热封方法、条件由供需双方商定。

　　7.5.3 拉断力和断裂标称应变

　　按GB/T 1040.3—2006 的规定进行。试样采用2 型，长度为150 mm，宽度为15 mm，试验速度

　　为200 mm/min。

　　7.5.4 直角撕裂负荷

　　按QB/T 1130 的规定进行。

　　7.5.5 抗摆锤冲击能

　　按GB/T 8809 的规定进行。

　　7.5.6 水蒸气透过量

　　按GB/T 1037 或GB/T 26253 的规定进行。温度为(38±0.5)℃，相对湿度(90±2)%。试验时

　　将热封面朝向湿度低的一侧。

　　GB/T 26253 为仲裁方法。

　　7.5.7 氧气透过率

　　按要求选用按GB/T 1038.1 或GB/T 19789 的规定进行。试验时将热封面朝向氧气低压侧。

　　GB/T 19789 为仲裁方法。

　　T/CPF 0096—2025

　　7

　　7.5.8 袋的耐压性能

　　7.5.8.1 试验装置

　　袋的耐压试验装置见图1。

　　标引序号说明：

　　1——砝码;

　　2——上加压板;

　　3——试验袋;

　　4——托板。

　　图1 耐压试验装置

　　7.5.8.2 试验步骤

　　袋内充约二分之一容量的水，并封口，样品为5 个。试验时将试样逐个放在加压板和托板之间。

　　试验中加压板和托板应保持水平、不变形，与袋的接触面应光滑，加压板和托板的面积应大于试验袋。

　　按表9 的规定加砝码，保持1 min(负荷为上加压板与砝码质量之和)，目视袋是否破裂或渗漏。

　　7.5.9 袋的跌落性能

　　按GB/T 10004 的规定进行。试验面为光滑、坚硬的水平面(如水泥地面)。袋内填充实际内

　　容物或约二分之一容量的水，试样数量为5 个。按表7 的规定将袋由水平方向和垂直方向各自由落

　　下一次，目视是否破裂。

　　7.5.10 摩擦系数

　　按GB/T 10006 的规定进行。

　　7.5.11 气密性

　　按GB/T 15171 的规定进行。

　　7.5.12 耐高温介质

　　在包装袋内分别装入4%乙酸(HAc)、1%硫化钠(Na2S)、5%氯化钠(NaCl)水溶液及精制

　　植物油，然后进行排气封口，在带反压冷却装置的高压灭菌锅中经121 ℃、40 min 高温加压处理，

　　并在压力保持不变的情况下冷却至室温取出，开袋后逐个检验外观，试验袋每组至少5 个。

　　将以上试验袋每组任取2 个，截取长度为150 mm 和宽度为15 mm 的长条形试样5 个，测定其

　　平均拉断力、伸长率、剥离力和热合强度。然后按公式(1)计算以上各测试项目的下降率，以%

　　表示，精确到个位数。

　　R A B 100

　　A

　　   ······························· (1)

　　式中：

　　R——被检测项目的下降率，单位为百分比(%);

　　A——耐高温介质试验前被检测项目的平均值;

　　B——经耐高温介质试验后被检测项目的平均值。

　　T/CPF 0096—2025

　　8

　　8 检验规则

　　8.1 组批

　　产品以批为单位进行检验，同一类别、同一厚度、同一工艺、同一原料连续生产的产品为一批，最

　　长连续生产时间不超过7 d 为一批。膜的最大批量不超过500 000 m2，袋的最大批量不超过1 500 000 只。

　　8.2 抽样方法

　　8.2.1 采用随机抽样方法。

　　8.2.2 对于袋样本，打开包装箱后随机抽取足够测试用的袋作为试验样本。

　　8.3 抽样方案

　　8.3.1 外观、印刷质量和规格尺寸

　　按GB/T 2828.1—2012 中检验水平为S-3，AQL=6.5 正常检查二次抽样方案执行，并按表8 判

　　定该批产品是否合格。卷膜的单位为卷，片膜的单位为张，袋的单位为只。

　　表8 外观、印刷和规格尺寸抽样方案

　　批量 样本 样本量 累计样本量 接收数Ac 拒收数Re

　　<500 第一

　　第二

　　5

　　5

　　5

　　10

　　0

　　1

　　2

　　2

　　501～3 200

　　第一

　　第二

　　8

　　8

　　8

　　16

　　0

　　3

　　3

　　4

　　3 201～35 000

　　第一

　　第二

　　13

　　13

　　13

　　26

　　1

　　4

　　3

　　5

　　35 001～500 000

　　第一

　　第二

　　20

　　20

　　20

　　40

　　2

　　6

　　5

　　7

　　≥500 001 第一

　　第二

　　32

　　32

　　32

　　64

　　3

　　9

　　6

　　10

　　8.3.2 袋的耐压性能、袋的跌落性能、耐热性和耐高温介质性

　　按GB/T 2828.1—2012 中检验水平为S-2，AQL=6.5 正常检查二次抽样方案执行，并按表9 判

　　定该项目是否合格。卷膜的单位为卷，袋的单位为只。

　　表9 袋的耐压性能、跌落性能、耐热性、耐高温介质性抽样方案和判定规则

　　批量 样本 样本量 累计样本量 接收数Ac 拒收数Re

　　1～35 000

　　第一

　　第二

　　5

　　5

　　5

　　10

　　0

　　1

　　2

　　2

　　≥35 001 第一

　　第二

　　8

　　8

　　8

　　16

　　0

　　4

　　3

　　5

　　8.3.3 拉断力、断裂标称应变、剥离力、热合强度、直角撕裂力、抗摆锤冲击能、氧气透过量和

　　水蒸气透过量

　　从已抽出样品中随机抽取一组试样进行测试。测试结果中若有不合格项，应再从该批中抽取双

　　倍样品复检不合格项，如仍有不合格，则判该项不合格。

　　8.3.4 批的合格判定

　　外观、印刷、尺寸及偏差、物理力学性能要求全部合格，则判该批产品合格。

　　8.4 出厂检验项目

　　对每批产品进行出厂检验，检验项目为：外观、印刷质量(印刷套印、印刷外观)、尺寸偏离、

　　T/CPF 0096—2025

　　9

　　剥离力和热合强度。

　　8.5 型式检验

　　型式检验项目为要求中规定的全部项目。有下列情况之一者，应进行型式检验：

　　a) 新产品或老产品转厂生产的试制定型鉴定;

　　b) 正式生产后，如结构、原料、工艺有较大改变，考核对产品性能影响时;

　　c) 正常生产过程中，1 年进行1 次检验;

　　d) 产品长期停产后，恢复生产时;

　　e) 出厂检验结果与前次型式检验结果有较大差异时。

　　9 标志、包装、运输和贮存

　　9.1 标志

　　产品的每件包装均应附有产品合格证，并标明产品名称、规格、数量、质量、批号、生产日期、

　　检验员代号、生产方名称、生产方地址、执行标准编号和贮存期等。

　　9.2 包装

　　采用瓦楞纸箱内衬塑料薄膜或纸箱外用封箱胶带、打包带封箱。

　　9.3 运输

　　运输中应防止碰撞和接触锐利物体，轻装轻卸，避免日晒、雨淋，保证包装完好及产品不受污

　　染。其标志方法按照GB/T 191 的规定进行。

　　9.4 贮存

　　产品应贮存于清洁、干燥、通风与温度适宜的库房内，避免阳光直射，距热源不小于 1 m，堆

　　放合理，贮存期自生产之日起为1 年。

　　T/CPF 0096—2025

　　10

　　参 考 文 献

　　[1] CEFLEX TR Designing for a circular economy — Recyclability of polyolefin-based flexible

　　packaging

　　中国包装联合会团体标准

　　包装用单一材质单向拉伸

　　聚乙烯复合膜、袋

　　T/CPF 0096—2025

　　*

　　北京科学技术出版社出版发行

　　(北京西直门南大街16 号 邮编：100035)

　　新华书店经销

　　河北泓景印刷有限公司印刷

　　版权专有 不得翻印

　　开本880×1230　1/16　印张0.75　字数21 千字

　　2025 年2 月第1 版　2025 年2 月第1 次印刷

　　*

　　书号：155714·758 定价：38.00 元

　　155714758

　　标准实施反馈与服务